Fiberlogy CPE HT filament 1.75, 0.750 кг (1.65 lbs)

Technical data and information

Diameter of filament: 1.75 mm
Dimensional tolerance of filament: +/- 0.02 mm
Oval tolerance: +/- 0.01 mm
Hotend: 260-280°C
Heated bed: 110-120°C
Closed chamber: not required
Fan: 0-25%
Flowrate: 95-105%
Printing Speed: < 100 mm/s
Surface: Masking tape, PVA glue, hairspray
Retraction (direct): 1-2 mm
Retraction (bowden): 4-6 mm
Retraction Speed: 20-45 mm/s
Drying conditions: 60°C / 4h
Notes: Due to the strong adhesion to the bed, it is not recommended to print directly on its surface or on glass. This can lead to damage. We recommend using a masking tape.

Physical properties	Test method	Unit	Typical value
Specific density	ISO 1183	g/cm3	1.18
Mechanical properties	Test method	Unit	Typical value
Tensile strength @ Yield	ISO 527	MPa	44
Tensile strength @ Break	ISO 527	MPa	52
Tensile modulus	ISO 527	MPa	1500
Elongation @ Yield	ISO 527	%	7
Elongation @ Break	ISO 527	%	200
Flexural strength	ISO 178	Mpa	62
Flexural modulus	ISO 178	MPa	1550
Izod Impact strength (Notched) @ 23°C	ISO 180	kJ/m2	92
Thermal Properties	Test method	Unit	Typical value
Heat Distortion Temperature @ 0.45 Mpa	ISO 75	°C	100
Heat Distortion Temperature @ 1.8 Mpa	ISO 75	°C	85
Vicat Softening Temperature	ISO 306	°C	110
Glass Transition Temperature Tg	DSC	°C	110
Meting Temperature Tm	DSC	°C	250
Continuous Use Temperature (UL Yellow Card)	UL 746	°C	95

Product descriptions

Fiberlogy CPE HT is a modern copolyester that stands out for its high mechanical and temperature resistance.

As member of the polymers family, which includes PET-G and PCTG, it surpasses them in terms of resistance to high temperatures, even up to 110°C.

Like other related materials, this filament has a high resistance to chemicals and lipids.

It is odourless and BPA, BPS and styrene free and can be used to create food contact parts.

CPE HT will find numerous applications that require resistance to degrading conditions, such as in a dishwasher or in the process of chemical sterilization or UV radiation.