Fiberlogy PA12 + CF5 filament 1.75, 0.500 kg (1.0 lbs) - black
|
Technical data and information
NYLON PA12+CF5
- Diameter of filament: 1.75 mm
- Dimensional tolerance of filament: +/- 0.02 mm
- Oval tolerance: +/- 0.02 mm
- Hotend: 255-270°C
- Heated bed: 90-110°C
- Closed chamber: required
- Fan: 0-10%
- Flowrate: 95-100%
- Printing Speed: 35-60 mm/s
- Surface: glass, masking tape
- Retraction (direct): 2-3 mm
- Retraction (bowden): 4-6 mm
- Retraction Speed: 20-45 mm/s
- Drying conditions: 80°C / 4h
- Notes: The material has highly abrasive properties. We recommend the use of hardened steel or ruby nozzles.
Wear gloves (the possibility of micro damages on the skin). Use a dust mask and protective glasses when processing.
| Physical properties |
Test method |
Unit |
Typical value |
| Specific density |
ISO 1183 |
g/cm3 |
1.05 |
| Mechanical properties |
Test method |
Unit |
Typical value |
| Tensile strength @ Yield |
ISO 527 |
MPa |
- |
| Tensile strength @ Break |
ISO 527 |
MPa |
60 |
| Tensile modulus |
ISO 527 |
MPa |
3050 |
| Elongation @ Yield |
ISO 527 |
% |
- |
|
Elongation @
Break
|
ISO 527 |
% |
10 |
| Flexural strength |
ISO 178 |
Mpa |
- |
|
Flexural modulus
|
ISO 178 |
MPa |
2900 |
|
Izod Impact strength (Notched) @ 23°C
|
ISO 180 |
kJ/m2 |
8 |
|
Thermal Properties
|
Test method |
Unit |
Typical value |
|
Heat Distortion Temperature @ 0.45 Mpa
|
ISO 75 |
°C |
160 |
|
Heat Distortion Temperature @ 1.8 Mpa
|
ISO 75 |
°C |
- |
|
Vicat Softening Temperature
|
ISO 306 |
°C |
160 |
|
Glass Transition Temperature Tg
|
DSC |
°C |
- |
|
Meting Temperature Tm
|
DSC |
°C |
178 |
|
Continuous Use Temperature (UL Yellow Card)
|
UL 746 |
°C |
- |
Product descriptions
- Increased tensile strength compared to Nylon PA12
- Higher stiffness compared to Nylon PA12
- Higher thermal resistance compared to unmodified Nylon PA12 (up to 160°C)
- High chemical resistance
- Anti-static properties
|