Grema 3D - Great Master LTD тел: +359 888 100 273
email: office@grema3d.com
Filaments %PROMO% Fiberlogy -> FiberFlex 30D -> Filament -> 1.75mm -> 0,850 kg/ 0,500 kg -> Orange

-43.17%
%PROMO% Fiberlogy -> FiberFlex 30D -> Filament -> 1.75mm -> 0,850 kg/ 0,500 kg -> Orange
Fiberlogy -> FiberFlex 30D -> Filament -> 1.75mm -> 0,850 kg/ 0,500 kg -> Orange
Fiberlogy -> FiberFlex 30D -> Filament -> 1.75mm -> 0,850 kg/ 0,500 kg -> Orange
Fiberlogy -> FiberFlex 30D -> Filament -> 1.75mm -> 0,850 kg/ 0,500 kg -> Orange

38.5€ 21.88€


  • NOTE: Free shipping is not included!
  • Made in the EU
  • Country of origin: Poland, Fiberlogy
  • 30D Shore hardness
  • High impact resistance in low temperatures
  • Very good thermal, chemical and abrasion resistance


Model
  • - 35.1 €
  • - 21.88 €


    • Размер


Technical data and information

The following parameters are only suggested print settings for this material.

To ensure the best print quality, it is necessary to choose the appropriate settings for a specific printer and printing conditions.

Diameter of filament: 1.75 mm

Dimensional tolerance of filament: +/- 0.05 mm

Oval tolerance: +/- 0.03 mm

Hotend: 200-220°C

Heated bed: 50°C-70°C

Closed chamber: not required

Fan: 75-100%

Flowrate: 105-110%

Printing Speed: <35 mm/s

Surface: glass, masking tape

Retraction (direct): 1-2 mm

Retraction Speed: 10-30 mm/s

Notes: To remove the print easier, it is recommended to heat the bed to 110°C

Mechanical properties Test method Unit Typical Value
Hardness Shore D2240, 1 sec, 23°C ISO 7619 ----------- 30
Hardness Shore A, 1 sec, 23°C ISO 7619 ----------- 81
Density ISO 1183 g/cm3 1.07
Break ISO 527 MPa 22
5% Strain ISO 527 MPa 1
10% Strain ISO 527 MPa 2
50% Strain ISO 527 MPa 6
Elongation at break ISO 527 % 870
Heat Distortion Temperature @ 0.45 MPa ISO 75 °C 70
Melting Temperature Tm DSC °C 170
Tear Strength ISO 34-1 kN/m 95


Подробно Product descriptions

FIBERFLEX 30D is characterized by reduced hardness up to 30D on the Shore scale, very good flexibility and higher impact strength.

The material is recommended especially for printing tires, seals, belts and all kinds of elastic elements.